Abstract

In this article, a phosphorus–nitrogen-containing flame retardant (DOPO-T) was successfully synthesized by nucleophilic substitution reaction between 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) and cyanuric chloride. The chemical structure of DOPO-T was characterized by Fourier transform infrared spectroscopy, proton nuclear magnetic resonance (NMR) and phosphorous-31 NMR, and elemental analysis. DOPO-T was then blended with diglycidyl ether of bisphenol-A to prepare flame-retardant epoxy resins. Thermal properties, flame retardancy, and combustion behavior of the cured epoxy resins were evaluated by differential scanning calorimetry, thermogravimetric analysis, limited oxygen index (LOI) measurement, UL94 vertical burning test, and cone calorimeter test. The results indicated that the glass transition temperature ( Tg) and temperature at 5% weight loss of epoxy resin (EP)/DOPO-T thermosets were gradually decreased with the increasing content of DOPO-T. DOPO-T catalyzed the decomposition of EP matrix in advance. The flame-retardant performance of EP thermosets was significantly enhanced with the addition of DOPO-T. EP/DOPO-T-0.9 sample had an LOI value of 36.2% and achieved UL94 V-1 rating. In addition, the average of heat release rate, peak of heat release rate, average of effective heat of combustion, and total heat release (THR) of EP/DOPO-T-0.9 sample were decreased by 32%, 48%, 23%, and 31%, respectively, compared with the neat EP sample. Impressively, EP/DOPO-T thermosets acquired excellent flame retardancy under low loading of flame retardant.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.