Abstract
A series of poly(aryl ether benzimidazole) copolymers bearing different aryl ether linkage contents were synthesized by condensation polymerization in polyphosphoric acid (PPA) by varying the feed ratio of 4,4′-dicarboxydiphenyl ether (DCPE) to terephthalic acid (TA). As the ether unit content in the copolymer increased, the solubility of the copolymer in PPA and N, N′-dimethylacetamide/LiCl improved. For example 3–7 wt.% DMAc solution containing 2 wt.% of LiCl could be prepared from the copolymers. XRD studies revealed that the incorporation of flexible aryl ether linkages increased the chain d-spacings of the polymer backbones and decreased the crystallinity of the copolymers. Still, these copolymers having ether linkages showed reasonably good thermal/mechanical stability and high proton conductivity. For example, the copolymer with 30 mol% ether linkage had a tensile strength of 43 MPa (at 26 °C and 40% relative humidity) at an acid doping level of 7.5 mol H 3PO 4 and a proton conductivity of 0.098 S cm −1 (at 180 °C and 0% relative humidity) at an acid doping level of 6.6 mol H 3PO 4.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.