Abstract
ABSTRACTHigh impact polystyrene (HIPS) resins were obtained with in situ bulk polymerization toughened by styrene–isoprene–butadiene terpolymer rubber (SIBR). SIBR prepolymer was prepared through selective polymerization of styrene (St), isoprene (Ip), and butadiene (Bd) in St with [Nd]/[Al]/[Cl] catalyst. Nd‐based catalyst exhibited more favorable activity toward conjugated diene other than St, resulting in St solution of random SIBR with high cis‐1,4 stereoregularity and low St content, which was directly exposed to the free radical polymerization of St to generate HIPS. Effect of toughened rubber and the initiators [difunctional (D2) and trifunctional (T3)] were examined to attain HIPS possessing mechanical properties as follow: impact strength, 0.9–24.8 kJ/m2; tensile strength, 16.0–27.5 MPa; and elongation at break, 7.4–107.0%. Increasing SIBR matrix in HIPS improved the impact strength and decreased tensile strength. The fracture surface morphologies of HIPS specimens were studied by notched impact tests and scanning electron microscopy (SEM), illustrating that the incremental SIBR matrix presented synergistic toughening effect of crazing to enhance the ductile fracture behavior. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016, 133, 43979.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.