Abstract
LiFe0.9Mg0.1PO4 sample was prepared by using a solid–state reaction method, and the temperature-dependent magnetic properties of the sample were studied. The X-ray diffraction (XRD) pattern showed an olivine-type orthorhombic structure with space group Pnma based on Rietveld refinement method. The effect of Mg substitution in antiferromagnetic LiFe0.9Mg0.1PO4 was investigated using a vibrating sample magnetometer (VSM) and Mössbauer spectroscopy. The temperature-dependence of the magnetization curves of LiFe0.9Mg0.1PO4 shows abnormal antiferromagnetic behavior with ordering temperature. Sudden changes in both the magnetic hyperfine field (Hhf) and its slope below 15K suggest that magnetic phase transition associated to the abrupt occurrence of spin-reorientation. The Néel temperature (TN) and spin-reorientation temperature (TS) of LiFe0.9Mg0.1PO4 are lower than those of pure LiFePO4 (TN=51K, TS=23K). This is due to the Fe–O–Fe superexchange interaction being larger than that of the Fe–O–Mg link. Also, we have confirmed a change in the electric quadrupole splitting (ΔEQ) by the spin-orbit coupling effect and the shape of Mössbauer spectrum has provided the evidence for TS and a strong crystalline field. We have found that Mg ions in LiFe0.9Mg0.1PO4 induce an asymmetric charge density due to the presence of Mg2+ ions at the FeO6 octahedral sites.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call