Abstract
A novel aromatic triamide 1,3,5-tri[4-(4-aminophenoxy)phenyl] benzene (TAPOPB) with prolonged chain segments and ether bonds was successfully prepared through a three-step reaction. Then a series of hyperbranched polyimides (HBPIs) were synthesized using A2 + B3 polycondensation from various commercial aromatic dianhydrides and TAPOPB. The HBPIs showed good solubility, thermal stability with glass transition temperatures ( Tg) between 218°C and 320°C, and temperature at 10% weight loss of 502.1–561.7°C in nitrogen atmosphere. Meanwhile, they had decent mechanical properties whose tensile strength and modulus were higher than 72.37 MPa and 1.039 GPa, respectively. Water uptake of less than 0.96% was obtained. The truncation wavelengths of the films were all greater than 400 nm with a good application prospect in UV protective coating. Most contact angles were more than 90°, promising to be used as hydrophobic material.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.