Abstract
Abstract High-purity microfine mullite precursor powder of stoichiometric chemical composition, 3Al2O3.2SiO2, was synthesized through the sol-gel route using aluminum isopropoxide and tetraethyl orthosilicate. The derived mullite precursor powder was characterized by BET surface area, particle size distribution, Fourier-transform infrared spectroscopy, thermogravimetry-differential thermal analysis (TG-DTA), X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy-dispersive X-ray spectroscopy. Phase analysis of the precursor powder and calcined samples at different temperatures was done by XRD. Non-isothermal crystallization kinetics of mullite precursor was studied by TG-DTA in static air using heating rates of 5.0, 7.5, 10.0, 12.5, and 15 K.min-1. Grain morphology was studied by SEM. The results showed that synthesized mullite precursor powder possessed homogeneity of Al and Si components, and the amorphous precursor powder was converted to monophasic mullite crystal when heat-treated at 970 °C. Based on Flynn-Wall-Ozawa and Kissinger equations, the activation energy associated with the crystallization of mullite was determined to be 1189.8 and 1189.0 kJ.mol-1, respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.