Synthesis and characterization of hydroxyapatite by microwave heating using CaSO4·2H2O and Ca(OH)2 as calcium source

Abstract

In this paper, synthesis of hydroxyapatite (HAp) in the absence or presence of 1.05 wt% magnesium oxide, as sintering additive, by heating in a microwave oven was studied. For this purpose, CaSO(4).2H(2)O, Ca(OH)(2), Mg(OH)(2) and (NH(4))(2)HPO(4) were used as raw materials. The total chemical reactions for all the studied compositions were observed after a 3 h microwave treatment. In case of pure hydroxyapatite, a powder with needle-like grains results. In the presence of Mg(OH)(2), the (Mg, Ca(2)).O.(HPO(4))(2).H(2)O hydrated phosphate is formed besides hydroxyapatite. Pure hydroxyapatite, thermally treated at 1,200 degrees C, mostly transforms in beta-Ca(3)P(2)O(8). By adding MgO into the precursor mixture, hydroxyapatite was stabilised, and found in a much greater proportion at 1,200 degrees C. After the thermal treatment, the hydroxyapatite, analysed by electronic microscopy, shows a prismatic morphology originating in its initial state.