Abstract
Variously substituted polyhedral oligomeric silsesquioxanes (POSSs)/polystyrene (PS) nanocomposites of general formula R7R′(SiO1.5)8/PS (where R = isobutyl and R′ = 4‐methoxyphenyl, 4‐methylphenyl, 3,5‐dimethylphenyl, 4‐fluorophenyl, 2,4‐difluorophenyl, 4‐chlorophenyl) were prepared by in situ polymerization of styrene in the presence of 5% w/w of POSS. The actual filler concentration in the obtained nanocomposites was checked by 1H NMR spectroscopy. Scanning electron microscopy and FTIR spectroscopy evidenced the presence of filler‐polymer interactions. Inherent viscosity (ηinh) determinations indicated that the average molar mass of polymer in halogenated derivatives was lower than neat PS, and were in agreement with calorimetric glass transition temperature (Tg) measurements. Finally, a comparative study concerning the thermal stability of synthesized nanocomposites was carried out in both inert (flowing nitrogen) and oxidative (static air) atmospheres into a thermobalance, in the scanning mode, at 10°C min−1, and the temperatures at 5% mass loss (T5%), of various compounds were determined. The results were discussed and interpreted. POLYM. COMPOS., 35:151–157, 2014. © 2013 Society of Plastics Engineers
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.