Synthesis and Characterization of Cu- and Co-Doped Bi4V2O11for Intermediate-Temperature Solid Oxide Fuel Cell Electrolytes by Carbonate Coprecipitation

Abstract

Bi2MexV1-xO5.5-3x/2 (Me = Cu; 0≤x≤0.2) powders were prepared by the ammonium carbonate coprecipitation method. The starting salts were bismuth nitrate, copper nitrate, cobalt nitrate, and vanadium sulphate. The thermal decomposition of Bi2MexV1-xO5.5-3x/2 precursors was completed at about 500 °C. The crystallite structure, surface morphology, and ionic conductivity of the prepared powders and pellets were examined using X-ray diffractometry, field emission scanning electron microscopy, and an impedance analyzer, respectively. The average particle sizes of the Bi2Cu0.1V0.9O5.35 and Bi2Co0.1V0.9O5.35 powders were 10–50 nm. The tetragonal structure (γ-phase) appeared at sintering temperatures higher than 700 °C and the peak intensity increased at higher sintering temperatures. The ionic conductivities of the Bi2Cu0.1V0.9O5.35 and Bi2Co0.1V0.9O5.35 pellets sintered at 800 °C showed the highest values of 6.8×10-2 S cm-1 at 700 °C and 9.1×10-2 S cm-1 at 700 °C, respectively. The optimum concentration of the Cu and Co dopants in Bi2MexV1-xO5.5-3x/2 was determined to be 0.1. The results of this study demonstrated that the ammonium carbonate coprecipitation process could be used as an economical method for the preparation of Bi2MexV1-xO5.5-3x/2 electrolytes for intermediate-temperature solid oxide fuel cells.