Abstract
In this research Cu-Ni nanostructure powders were prepared by using a chemical procedure including initial precipitating, calcining the precipitates and reducing the calcined powders. The influence of nickel contents on the characteristics of the synthesized powders was investigated. Copper and nickel sulfate and sodium hydroxide were used as raw materials. CuSO4.3Cu(OH)2, NiOOH and Ni(OH)2 precipitates were obtained by addition of sodium hydroxide into aqueous copper and nickel sulfate solution. Oxide powders were produced by calcinations of precipitates. Considering the information obtained from the TGA test, calcination was done on precipitates. Copper-nickel nanostructure powders were synthesized by reduction of calcined powders in a hydrogen atmosphere. Eventually powders were characterized by using X-ray diffraction (XRD) and scanning electron microscopy (SEM). Crystallite size of final synthesized powders was in the range of 30 to 33 nm.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.