Abstract
The cBN/cemented carbide containing 30vol% of cBN particles was produced using a mixture of a 6wt% Co added-WC powder, with a WC grain size of 0.4 μm and a cBN powder with a grain size ranging from 4 to 40 μm. The mixture was sintered to produce a plate, 20 mm in diameter, 3 mm thick. The sintering processes were conducted at temperature of 1100°C under a load of 100 MPa. The phase composition, density, hardness and micro structure of the sintered parts thus obtained were examined. The fractures through the WCCo/cBN composite showed the cBN particles torn out from the cemented carbide matrix were only few, whereas most of them have cleaved along the fracture plane. This gives evidence that the bond at the WCCo/cBN interface is mechanically strong.