Abstract
In this research, a novel ethylene propylene diene monomer rubber (EPDM) formulation for cable with high ceramization efficiency was prepared by the addition of functionalized sepiolite with boron fluxing compound nanoparticles (SEPTB) obtained by precipitation route. Non-functionalized sepiolite (SEP) has been incorporated to the system for reference. EPDM materials were characterized by standardized tests measuring their behavior against fire and important improvements were observed, especially in terms of smoke production (25% reduction of the smoke production compared with the formulation using SEP) presenting a remarkable behaviour against dripping and self-extinction when a flame is directly applied. The mechanism of ceramization under fire conditions was discussed. It was found that EPDM system with SEPTB additive transformed into a rigid ceramic after treating at 1000°C. In this particular case, the ceramization was more efficient due to the sepiolite transformation to enstatite at lower temperatures (∼750 vs ∼850°C) combined with the “in situ” formation of a glassy phase which notably enhances the reinforcement of the char layer by forming a reinforcing 3D ensatite fibers net structure that reduces smoke production and even totally avoids the dripping of melted polymer by the action of the heat in a fire event. This work provides new insights for the preparation of high-performance synergist additive based on sepiolite for the enhancement of fire retardance of EPDM system for cable applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Boletín de la Sociedad Española de Cerámica y Vidrio
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.