Abstract
AbstractSwitching current measurements have been carried out on relaxorferroelectric single crystal-pure PZN, and the solid solution (1-x) Pb(Zni1/3 Nb2/3)O3 - x PbTiO3 with x= 0.04, 0.09, 0.10. Measurements have been done for crystallographic directions [001] and [111] for all these compositions. Switching times versus the applied field showed the following results. Pure PZN along [111] and 0.90PZN—O. 10PT along [001], and [111] showed an exponential dependence. Along [001] the PZN showed a linear fit. For solid solution single crystals-0.96PZN -0.04PT and 0.91PZN £ 0.09PT, a linear fit was obtained for the reciprocal switch times versus applied field for both the directions. If we draw a parallel picture with the reported barium titanate data, it appears that the polarization reversal is controlled by nucleation along [111]- spontaneous direction for PZN and [001], [111]for 0.90PZN - O.10PT. The mobility of the reversed domains controls the reversal along [001] for PZN and the solid solution single crystals with rhombohedral composition along [001] and [111]. The transient current curves showed two maximum points for crystals with x = 0.04 and 0.09. This is attributed to the co-existence of the two phases in 0.96PZN -0.04PT and 0. 91PZN - 0.09PT crystals.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.