Abstract

Non-toxic inorganic pigments based on the Fe(III)-doped YAlO3 with high near-infra-red (NIR) reflectance were synthesized by a modified Pechini method at 1200 °C. A complete solid solution in the YAl1−xFexO3 system (0 ≤x ≤ 1) was prepared, yielding a wide range of colourations from yellow to red, depending on the iron content.Good pigment stability was achieved in a commercial high temperature glaze, used in the ceramic industry to colour glazes on tiles. The pieces coated with the pigmented glazes reached NIR solar reflectance values between 43% and 32%. The temperature protection studies carried out with the glazes pigmented with YAl0.75Fe0.25O3 and YFeO3 compositions, conclude that the pigmented samples reduce the temperature of a building by 5 °C and 4 °C, respectively, in comparison to the unpigmented glaze.Thus, these pigments can be excellent candidates for used in high-temperature applications such as colouring ceramic high temperatures glazes, as well as cool pigments in walls or roofs of buildings.

Full Text
Published version (Free)

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call