Abstract
The aluminum alloys AA5052, AA5083 and Al-7%Si (AC4C) were nitrided by electron beam excited plasma (EBEP) technique to improve wear resistance and hardness. The specimens were characterized with respect to the following properties: wear resistance, hardness of nitrided layer (AlN layer), surface and cross sectional microstructures. The friction coefficient of nitrided AA5052 decreased to 0.2 and that of Al-7%Si was improved to 0.1. The AlN layers were relatively uniformly formed on the AA5052 and AC4C alloys with a thickness of 4.5 μm and 2.5 μm during 2hrs and 5.4 ks, respectively. On the surface of nitrided AA5083, a uniform AlN layer was not formed due to the high nitriding temperature. The Si3N4 was found in the nitrided AC4C alloy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.