Abstract
REBa 2 Cu 3 Oy (REBCO, RE = rare earth) coated conductors are required for high current carrying capability. Self-organization of Ba-M-O (BMO, M = Zr, Sn, Hf...) is available to improve critical current density (J c ) in magnetic field, and suppression of a-axis grain growth contributes to enhance J c . The former and latter are affected by the surface diffusion of adatoms and supersaturation in the REBCO film growth, respectively. We focused on surface morphologies of SmBa 2 Cu 3 O y (SmBCO) films deposited by the pulsed laser deposition method in this paper, and estimated surface diffusion constant and supersaturation from the surface morphologies. As a result, an activation energy of the surface diffusion was approximately 2.2 eV and the value is somewhat smaller than 2.5 eV for YBCO films. Additionally, we found that a-axis grains appeared when supersaturation (Δμ) became higher than a threshold Δμ . Interestingly, a seed layer consisting of c-axis oriented SmBCO suppressed a -axis grain growth. These findings are useful to improve J c in REBCO coated conductors.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.