Abstract
This study evaluated roughness parameters and phase transformation of monolithic zirconia ceramics after various mechanical and laser thermal treatments. Fully sintered monolithic zirconia cylinder specimens were divided to five groups, according to the applied surface treatment: CL: control, GB: grit-blasted with glass particles. AL50: grit-blasted with 50 μm alumina particles, AL90: grit-blasted with 90 μm dyed-alumina particles and FEML: subjected to femto laser thermal treatment. Six roughness parameters (Sa, Sq, Sz, Sci, Svi and Sdr) were measured by optical profilometry. Phase transformation in zirconia was determined by micro-Raman spectroscopy. The highest roughness values were recorded in AL90 and FEML groups, followed by AL50. AL90 presented statistically higher monoclinic phase content compared to all other groups. Control and GB groups presented similar roughness without phase transformation. Laser thermal treatment causes minimal destruction of the zirconia surface, and can be suggested as an alternative to other roughening treratments, for enhancing the adhesive potential to dentin.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.