Surface biomedical effects of plasma on polyetherurethane

Abstract

Surface biomedical effects of plasma treatment and plasma polymerization on medical-grade polyetherurethane were studied. N2 and Ar plasma treatments and hexamethyldisiloxane (HMDS) plasma polymerization were performed at a power of 100 W with exposure times ranging from 1 to 15 min. The results showed that the contact angle of water was decreased from 79° to 62° by N2 and Ar plasma treatments, and N2 plasma treatment caused a slight enhancement in anti-coagulability and anti-calcific behavior. HMDS polymerization resulted in a decrease from 79° to 43° in the contact angle and an increase from 30.5 to 37.4 s in the recalcification time. At the same time, the anti-coagulability of polymerized samples for the exposure time of 2-5 min was 2.5 times that of the untreated sample. Results of XPS and ESR analyses showed that HMDS deposited onto the polyetherurethane surface and formed new Si-N bonds, and increased the number of radicals in the sample. XPS analysis also showed that N2 and Ar plasma treatments bro...