Abstract
Two different kinds of two-dimensional (2D) materials, graphene oxide (GO) and titanium oxide nanosheets (Ti₀.₈₇O2(0.52-)), were self-assembled layer-by-layer using a polycation as a linker into a superlattice film. Successful construction of an alternate molecular assembly was confirmed by atomic force microscopy and UV-visible absorption spectroscopy as well as X-ray diffraction analysis. Exposure of the resulting film to UV light effectively promoted photocatalytic reduction of GO as well as decomposition of the polycation, which are due to their intimate molecular-level contact. The reduction completed within 3 hours, bringing about a decrease of the sheet resistance by ∼10(6). This process provides a clean and mild route to reduced graphene oxide (rGO), showing advantages over other chemical and thermal reduction processes. A field-effect-transistor device was fabricated using the resulting superlattice assembly of rGO/Ti₀.₈₇O₂(0.52-) as a channel material. The rGO in the film was found to work as a unipolar n-type conductor, which is in contrast to ambipolar or unipolar p-type behavior mostly reported for rGO films. This unique property may be associated with the electron doping effect from Ti₀.₈₇O₂(0.52-) nanosheets. A significant improvement in the conductance and electron carrier mobility by more than one order of magnitude was revealed, which may be accounted for by the heteroassembly with Ti₀.₈₇(0.52-) nanosheets with a high dielectric constant as well as the better 2D structure of rGO produced via the soft photocatalytic reduction.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.