Superior Storage Performance of a Si@SiOx/C Nanocomposite as Anode Material for Lithium‐Ion Batteries

Abstract

Rechargeable lithium-ion batteries are essential to portable electronic devices. Owing to the rapid development of such equipment there is an increasing demand for lithium-ion batteries with high energy density and long cycle life. For high energy density, the electrode materials in the lithium-ion batteries must possess high specific storage capacity and coulombic efficiency. Graphite and LiCoO2 are normally used and have high coulombic efficiencies (typically >90%) but rather low capacities (372 and 145 mAhg, respectively).[1–5] Various anode materials with improved storage capacity and thermal stability have been proposed for lithium-ion batteries in the last decade. Among these, silicon has attracted great interest as a candidate to replace commercial graphite materials owing to its numerous appealing features: it has the highest theoretical capacity (Li4.4Sio4200 mAhg) of all known materials, and is abundant, inexpensive, and safer than graphite (it shows a slightly higher voltage plateau than that of graphite as shown in Figure S1, and lithiated silicon is more stable in typical electrolytes than lithiated graphite[6]).