Abstract
Superhydrophobic nanofibers have received prominent attention owing to their exceptional properties and researchers are focused on developing high-performing MD membranes. Herein, we fabricate superhydrophobic electrospun nanofibrous membranes using polyvinylidene fluoride (PVDF) solutions with silica nanoparticles (0 wt% to 6 wt%) to create multiscale (or hierarchical) surface roughness. For superhydrophobicity, the composite membranes (Si@PVDF) were subjected to a two-step modification that included acid pre-treatment and silanization with fluoroalkylsilane (FAS) compound of low surface energy. The acid pre-treatment enhances the hydroxyl group of SiO2 nanoparticles and create active sites in abundance for silanization. The modified membranes (FAS-Si@PVDF-A) having 6 wt% SiO2 showed excellent wetting resistance with water contact angle (WCA) up to 154.6 ± 2.2°, smaller average pore size of 0.27 ± 0.3 μm, and high liquid entry pressure (LEP) of 143 ± 4 kPa. It was observed, increasing silica content decreased the fiber diameter and average pore size and increased WCA and LEP of modified membranes. The modified superhydrophobic membranes gave stable permeate flux, exhibited strong wetting resistance and excellent salt rejection in vacuum membrane distillation (VMD) test. The optimal FAS-Si@PVDF-A membrane (6 wt% SiO2) of thickness 98 ± 5 μm produced a stable permeate flux of more than 11.5 kg m−2 h−1 and salt rejection as high as 99.9% after 22 h of continuous operation using NaCl solution (3.5 wt%) as feed. Therefore, this modification provided superhydrophobic membranes possessing robust anti-wetting properties with significant permeability and has encouraging application in membrane distillation for desalination.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.