Abstract
Performance and reliability of microelectromechanical system (MEMS) components can be enhanced dramatically through the incorporation of protective thin-film coatings. Current-generation MEMS devices prepared by the lithographie-galvanoformung-abformung (LIGA) technique employ transition metals such as Ni, Cu, Fe, or alloys thereof, and hence lack stability in oxidizing, corrosive, and/or high-temperature environments. Fabrication of a superhard self-lubricating coating based on a ternary boride compound AlMgB14 described in this letter has great potential in protective coating technology for LIGA microdevices. Nanoindentation tests show that the hardness of AlMgB14 films prepared by pulsed laser deposition ranges from 45 GPa to 51 GPa, when deposited at room temperature and 573 K, respectively. Extremely low friction coefficients of 0.04–0.05, which are thought to result from a self-lubricating effect, have also been confirmed by nanoscratch tests on the AlMgB14 films. Transmission electron microscopy studies show that the as-deposited films are amorphous, regardless of substrate temperature; however, analysis of Fourier transform infrared spectra suggests that the higher substrate temperature facilitates the formation of the B12 icosahedral framework, therefore leading to the higher hardness.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.