Abstract
Phase change materials (PCMs) when amalgamated in a shell material to form microencapsulated-PCMs (MPCMs) usually exhibit high levels of supercooling due to the limited crystallization process. In the present study, various efforts were made to reduce this phenomenon, including increasing the MPCM size, employing nucleating agents, and embedding copper nanoparticles into the MPCM shells. It was observed that with an increase in the microcapsule size from 43 μm to 76 μm, the supercooling was reduced by a value of 10.2 °C from melting/freeing point peak temperature differences of 37.6 to 27.4 for the 1200 rpm and 800 rpm samples respectively. Comparatively, the implementation of octadecanol nucleating agent 30 wt % resulted in a reduction of supercooling by 22.9 °C. The introduction of Cu nanoparticles with a decane core can also reduce the supercooling degree by 4.6 °C, while the thermal conductivity the MPCM samples with a hexadecane core increased from 0.173 to 0.182 W m−1 K−1 before and after the addiction of the Cu nanoparticles. Furthermore, di(propylene glycol) methyl ether was used as a carrier fluid for the MPCMs to study the slurry rheological behaviors with various MPCM compositions. It was observed that the MPCM suspension with 10–20% MPCM mass concentration did not exhibit shear thinning, while the 30% sample conveyed shear thinning properties. Furthermore, near the crystallization temperature of the PCM, the slurry viscosity sharply rose, attributed to the volume changes and non-cooperative motion of MPCM microcapsules.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.