Abstract
Abstract In the present work it is described the production of MgB2 samples by using the mixture of MgB2 with other diborides, (TaB2, VB2, and AlB2) which have the same C32 hexagonal structure as the MgB2, and simultaneous addition with the diborides and SiC, that contribute with C, to replace B in the crystalline structure of the matrix. As an important result, the critical current density ( Jc ) was improved at low magnetic fields when just the diborides are added. However, when SiC is added simultaneously with the diborides, the result is the improvement of Jc at high fields. The critical temperature ( Tc ) was maintained high.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.