Abstract
Superconducting joints between single-core MgB2/Ni and MgB2/Nb wires made by an internal Mg diffusion (IMD) process have been manufactured by using scarf joints architecture. Joint’s transport current were measured at 4.2 K and external magnetic fields of 2–8 T and compared with the currents of used MgB2 wires. Structure of selected joints were analysed by an optical microscope. It was found that addition of boron powder between the joined wires allows the creation of superconducting current paths. Observed Mg–Ni interaction inside the joint area reduces the creation of well-connecting MgB2 phase, and consequently, degrades the critical current of joint by 6.7% of wire’s Ic. Joints between MgB2/Nb wires have no inter-metallic interactions, and consequently, large critical currents up to 60% of wire’s Ic can obtained. Presented results show that wires with inert metallic sheath and added boron powder could be used for the fabrication of applicable superconducting joints and MgB2 coils working in persistent mode.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.