Abstract
High-performance biosourced polylactic acid (PLA)/poly(butylene succinate) (PBS) blends with small amounts of compatibilizer, epoxy-functionalized methyl methacrylate-co-glycidyl methacrylate copolymer (PMMA-GMA), were fabricated by melt compounding. The properties of the modified PLA/PMMA-GMA, PBS/PMMA-GMA, and PLS(PLA/PBS)/PMMA-GMA blends were investigated systematically. DSC combined with X-ray diffraction revealed a low-order semi-crystalline structure for all samples. SEM and DMA showed that the compatibility between PLA and PBS was improved after addition of PMMA-GMA. Rheological behavior of blends showed that the addition of PMMA-GMA resulted in a significant improvement in the viscoelasticity. FT-IR spectra confirmed that the interfacial compatibilization between PLA and PBS phases was improved due to the reaction of epoxy groups with terminal groups of PLA and PBS. Finally, the toughness and notched impact strength of the PLA materials were increased significantly. The elongation at break and notched impact strength of PLS/PMMA-GMA was about 55.7 and 6.2 times than neat PLA after incorporation of 7 wt% PMMA-GMA, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: International Journal of Biological Macromolecules
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.