Abstract
Two hot‐pressed sintered α‐sialon samples of differing microstructures, but identical chemical composition, were evaluated first, in terms of indentation hardness and modulus, by depth‐sensing indentation (DSI) tests on planes parallel and normal to the hot‐pressed surface. The surface and subsurface cracks created under the DSI tests have also been investigated in relation to the effect of microstructure. Subsequently, Vickers indentation tests were conducted to explore the deformation and fracture characteristics in the two samples. The effect of microstructure and grain orientation on the development of different types of cracks, in particular subsurface cracks, was revealed and analyzed. Additionally, it suggested that the focused ion beam (FIB) miller is a preferred tool, in comparison to the conventional cross‐sectioning techniques, for examining subsurface crack formation and structural characteristics.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.