Abstract
Abstract Single crystals of magnesium containing varying amounts of In, Al, Pb and Bi in solid solution have been deformed in tension over a range of temperature between 4.2°k and 500°k. The critical resolved shear stress (CRSS) for basal slip has been examined in the light of the existing solution hardening theories. The earlier published data on Zn, Cd, Tl and Li solutes were included in arriving at a generalized solution hardening model for magnesium. The CRSS in the plateau region (above 295°k) can be described best with a C 2/3 relationship, where C is the atom fraction of solute. The strengthening mechanism was found to be one involving the interaction of solute atoms with edge dislocations. The extent of hardening is determined by the size and valency differences between the solute and the solvent. The valency term was found equivalent to the modulus interaction term of the statistical solution hardening theories. The CRSS at 0°k increases linearly with alloying at concentrations of solute above 0....
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.