Study the Effect of Liquid Layer Level on the Formation of Zinc Oxide Nanoparticles Synthesized by Liquid-Phase Pulsed Laser Ablation

Abstract

This work is focused on studying the effect of liquid layer level (height above a target material) on zinc oxide nanoparticles (ZnO and ZnO2) production using liquid-phase pulsed laser ablation (LP-PLA) technique. A plate of Zn metal inside different heights of an aqueous environment of cetyl trimethyl ammonium bromide (CTAB) with molarity (10-3 M) was irradiated with femtosecond pulses. The effect of liquid layer height on the optical properties and structure of ZnO was studied and characterized through UV-visible absorption test at three peaks at 213 nm, 216 nm and 218 nm for three liquid heights 4, 6 and 8 mm respectively. The obtained results of UV–visible spectra test show a blue shift accompanied with decreasing the liquid level above the target due to the increase in ablation rate and particles production. This blue shift indicates getting a smaller size of nanoparticles and the quantum confinement property of nanoparticles. Also the FTIR transmittance spectra of ZnO2 nanoparticles prepared in these states show a characteristic ZnO absorption at 435 cm−1 – 445 cm−1.