Abstract
AbstractThe mechanical, friction and wear properties of different modified polyoxymethylene (POM) are presented in the paper under free abrasive grinding condition. The shore hardness and elastic modulus of the POM matrix increased with carbon fiber (CF) filling, its shore hardness and elastic modulus were 85 HD and 5000 MPa, respectively. The hardness and elastic modulus of the POM matrix decreased with polytetrafluoroethylene (PTFE) and graphite (C) filling. The average coefficient of friction of POM was 0.254. When PTFE, CF, and graphite were added, the coefficient of friction of the POM would be reduced under free abrasive condition. The coefficient of friction of POM filled with PTFE or graphite was about 0.15, the coefficient of friction of POM filled with CF was about 0.18. It could be seen from the orthogonal test analysis that the wear resistance of four types of materials was CF‐POM > POM > PTFE‐POM > C‐POM. When the test duration was 1.5 h, the wear amount of C‐POM was between 3 and 9 mg, the wear amount of CF‐POM was less than 1.23 mg. The speed and load were the main factors affecting the wear amount of these materials, followed by the abrasive particle diameter, and the abrasive mass fraction had the least effect on them.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.