Abstract
The ferroelectric properties of UV irradiated and non-irradiated SBT thin films using photosensitive starting precursors were investigated. The observation of surface microstructure showed that UV irradiation and increase in anneal temperature induced the grain growth of SBT. The measured remnant polarization values of UV irradiated and non-irradiated SBT films after anneal at 700oC were 5.8 and 4.7 )C/cm2 and after anneal at 750oC, the values were 10.8 and 9.3 )C/cm2, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.