STUDY ON PROPERTIES OF SISAL FIBER REINFORCED CONCRETE WITH DIFFERENT MIX PROPORTIONS AND DIFFERENT PERCENTAGE OF FIBER ADDITION

Abstract

The present research was designed to check the workability and strength properties of sisal fiber reinforced concrete with different mix proportions and different percentage of fiber addition. The materials were chosen to improve the various strength properties of the structure to obtain sustainability and better quality structure. Short discrete vegetable fiber (sisal) was examined for its suitability for incorporation in cement concrete. The physical property of this fiber has shown no deterioration in a concrete medium. Fibers were brushed, lined up and cut to obtain 4cm length. Degree of workability of concrete mix with 0.2% super plasticizer and water cement ratio 0.45 had good workability with slump value 53mm and compaction factor 0.88, which is effective, was obtained. Materials were hand mixed with 0.5%, 1% and 1.5% addition of fiber in M20 and M25 mix design and casted in cubes and cylinders. The obtained specimens were subjected to tests aimed to check the compressive, tensile and flexural strength. An increase in compressive strength by 50.53% and tensile strength by 3.416% was observed for 1.5% addition of fiber in M20 mix design respectively. An increase in compressive strength by 52.51% and tensile strength by 3.904% was observed for 1.5% addition of fiber in M25 mix design respectively.