Abstract
The present work reports on resistive switching (RS) characteristics of Neodymium (Nd)-doped bismuth ferrite (BFO) layers. The Nd (2–10 at%) doped BFO thin film layers were deposited using a spray pyrolysis method. The structural analysis reveals that a higher Nd doping concentration in BFO leads to significant distortion of the prepared Nd:BFO thin films from rhombohedral to tetragonal characteristics. The morphological analysis shows that all the deposited Nd:BFO thin films have regularly arranged grains. The X-ray photoelectron spectroscopy (XPS) analysis reveals that the prepared Nd:BFO thin films have a higher Fe 3+/Fe 2+ratio and less oxygen vacancy (VO) defects which enriches the ferroelectric characteristics in Nd:BFO layers. The polarization-electric field (P-E) and RS characteristics of the fabricated Nd:BFO-based RS device were examined. It was observed that the Nd (7 at%) doped BFO RS device shows large remnant polarization (P r) of 0.21 μC/cm2 and stable RS characteristics.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call