Abstract
Effect of liquid electrolysis-free boriding on tribotechnical characteristics of 08Kh18N10Т steel is studied. It is established that after boriding at temperature 900 °С and 5 h soaking it is formed a boride two-phase layer with thickness of 30...35 microns and transition zone with thickness of 10 microns. The microhardness in FeB and Fe2B phases is 2000...2100 and 1800...1900 HV 0.1 respectively. The wear tests under dry friction conditions showed that coefficient of friction for specimens made of 08Kh18N10Т steel without treatment and with boriding in pair with counterbody made of ShKh15 steel is 0.83 and 0.85 respectively. At the same time, the wear intensity of samples with boration is an order of magnitude less than that of samples without treatment, and on average is 7.7 · 10–6 mm3 /(H · m) instead of 8.5 · 10–5 mm3 /(H · m). The average depth of the wear track of the sample with boriding is 5 times less than that of the sample without treatment.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Blanking productions in mechanical engineering (press forging, foundry and other productions)
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.