Abstract
Hybrid Nb(tNb)/Co(10nm)/IrMn(15nm)/Nb(10nm) heterostructured materials were prepared by DC Magnetron Sputtering and systematically studied by X-ray, magnetization and ferromagnetic resonance techniques. For thinner Nb buffer layer (≤10nm), it was found that there is an inter-diffusion at Co/IrMn interface, which favors double-like hysteresis loop. For thicker Nb layers, however, a gradual transition from double to single-like hysteresis loops is observed and it is associated with the reduction of the Nb roughness, which also enhances the exchange coupling at the Co/IrMn interface. Nb grown on IrMn layer induces the formation of an NbIrMn alloy layer, while no evidence of inter-diffusion at the Co/Nb interface is observed. For rougher Nb buffer layers (tNb<50nm), exchange bias and Co uniaxial anisotropies are pointing at the same direction (β∼zero), but for smoother Nb buffer layer (tNb=50nm) a β angle of 150o is found. Exchange bias effect was measured in as-prepared and in field-cooled samples; being its presence, in as-prepared sample, attributed to the unidirectional anisotropy of the Co layer (its intensity is modified in case of sample with a CoIrMn alloy layer). Considering that the Si/Nb/Co/IrMn interfaces have different β values (tNb=35 and 50nm), a study of the influence of magnetization direction, governed by exchange-biased layers, on superconducting properties of Nb films can be successfully done in this hybrid system.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call