Study of the growth mechanism of highly in-plane aligned α-axis YBa2Cu3O7−x thin films on LaSrGaO4 substrate by high resolution electron microscopy

Abstract

Highly in-plane aligned α-axis YBa2Cu3O7−x thin films deposited on (100) LaSrGaO4 substrates by a self-template method were studied by high-resolution electron microscopy along three orthogonal 〈100〉 axes of the substrate. Plan-view images confirm that the majority of the film preferentially aligns across the entire substrate except for very few misaligned domains with average size 10 nm2. Cross-sectional images along the [100] orientation of YBa2Cu3O7−x reveal that in-plane aligned α-axis YBa2Cu3O7−x is grown on a template layer dominated by c-axis oriented film. This strongly suggests that the in-plane alignment of α-axis YBa2Cu3O7−x thin films on (100) LaSrGaO4 substrates is governed by the different stresses along the b and c axes of the substrate. Cross-sectional images along [001] of the YBa2Cu3O7—x thin film reveal that the 90° domains easily nucleate in the region between α-axis YBa2Cu3O7—x and the YBa4Cu3Ox phase. Cracks along the (001) plane of YBa2Cu3O7−x are found to be due to the large mismatch between the c parameters of the thin film and substrate.