Study of the effect of heat temperature on the chemical changes and hygroscopicity of eucalyptus wood by FT-IR and prediction of mechanical properties by the MLR regression method

Abstract

This study describes the effect of heat treatment on some physical, chemical, and mechanical properties of Eucalyptus Camaldulensis (EC) wood at different temperatures and treatment times (200 °C–260 °C for 5, 60, and 90 min). The evaluation of hygroscopic properties was determined by relative humidity, mass loss, dimensional stability tests, and density. The results showed that the heat treatment leads to an increase in mass loss of 5.2 %–11.9 % at 200 °C. The density changed significantly for this studied species as well as the dimensional stabilization. Chemical changes in wood structure were assessed by Fourier Transform Infrared Spectroscopy.To verify the validity of the superposition “Mass loss-Density-water absorption” on the mechanical properties (modulus of elasticity (MOE) and modulus of rupture (MOR)) during heat treatment, we have developed a mathematical model based on Multiple Linear Regression (MLR), in order to establish a relationship between the independent parameters and the dependent parameters (MOE and MOR). The evaluation of the quality of the models developed was based on several statistical tools, namely R = 0.99, R2 = 0.99, R2adj = 0.98, and F = 132.33. The results demonstrated that elaborate models of mechanical properties have a high predictive capacity (MOR and MOE). The wood’s carbohydrates (particularly hemicelluloses) are then degraded during the heat treatment. The % of carbon increases from 47.8 to 49.8 %, which is proportional to mass loss, while the % of oxygen decreases by 46.1 %, which is inversely proportional to mass loss. Furthermore, FTIR analysis revealed that the effect of heat-treated wood chemical changes was related to the hydroxyl OH function of cellulose, functional groups, and aromatic system of lignin. In conclusion, the results demonstrated that at 200 °C, heat treatment caused a 5.2–11.9 % increase in mass loss; dimensional stability and density underwent considerable changes. FTIR spectroscopy confirmed the chemical changes in the wood structure during heat treatment. Furthermore, the “MLR” mathematical model showed that density contributed to the increase in MOR and MOE properties, while water absorption and mass loss contributed to the decrease in MOR and MOE properties. Finally, the % of oxygen decreased by 46.1 %, which is inversely proportional to the loss of mass, and the % of carbon increased from 47.8 % to 49.8 %, which is proportional to the loss of mass.