Abstract
The properties of nano Al2O3modified electrolytic phosphating film have been studied through using the accelerated corrosion test, electrochemical testing techniques, scanning electron microscope (SEM) and X-ray diffraction (XRD) .The results show that, after adding nano- Al2O3 in electrolytic phosphating bath , morphology of phosphating film surface turned dense flake crystallization from needle crystal morphology of free-adding nano- Al2O3powder, and the value of impedance of the Al2O3incorporated phosphate coating was increased obviously.When the nano- Al2O3concentration was 15mg / L in electrolytic phosphating bath, the value of impedance of the coating is approximately two times larger than the phosphating coating directly formed on the low carbon steel.The corrosion resisting time of the coating was more than 420 s by CuSO4dripping test, and the corrosion current density of the phosphating sample was 1.164μA/cm2，in 3.5% NaCl solution, the corrosion inhibition efficiency reached 96.7%.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.