Abstract
Degradation behavior of coated magnesium alloys is among most prominent factors for their biomedical applications. In this study, bio-corrosion behavior of micro-arc oxidized magnesium AZ31 alloys formed in silicate and phosphate baths was investigated in r-SBF medium. For this purpose polarization behavior and open circuit profile of the coated samples were achieved by electrochemical and immersion tests, respectively. Moreover, the morphology and composition of the coatings were evaluated before and after immersion test using scanning electron microscopy, X-ray diffraction and energy dispersive spectroscopy. The results showed that the phosphate film had better corrosion resistance and greater thickness than silicate film and, in turn, the lesser degradability in SBF solution, so that Ca2+ and PO43− containing compounds were more abundant on silicate film than phosphate film. Moreover phosphate film had greater surface roughness and lesser hydrophilic nature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.