Abstract
In this work, Cu-based microcomposites were fabricated by powder metallurgy of gas-atomized Cu-15wt% Fe alloy powder, followed by drawing to various strains. The microstructure evolution and the resultant mechanical and electrical properties were investigated by scanning electron microscopy, electron backscatter diffraction, and tensile testing, among other techniques. The results indicated that during drawing, the Fe phase evolved into nanoscale filaments along the longitudinal direction. With increasing drawing strain, both the Cu grains and the Fe filaments were refined gradually, giving rise to a mean thickness of approximately 25nm for the Fe filaments at a total strain of 4.0. The iron oxides particles formed due to contamination of oxygen maintained unchanged during drawing process. In addition, it was found that an intermediate aging during the drawing can significantly enhance the electrical conductivity of the microcomposites without sacrificing their strength. The present process involving an initial powder with a homogenous distribution of Cu and fine Fe phases makes it possible to obtain microcomposites with an ideal combination of electrical and mechanical properties at lower drawing strain, compared to those produced by conventional casting methods.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.