Abstract
The effect of alkaline hydrothermal activation of class-C fly ash belite cement was studied using thermal analysis (TG/DTG) by determining the increase in the combined water during a period of hydration of 180 days. The results were compared with those obtained for a belite cement hydrothermally activated in water. The two belite cements were fabricated via the hydrothermal-calcination route of class-C fly ash in 1 M NaOH solution (FABC-2-N) or demineralised water (FABC-2-W). From the results, the effect of the alkaline hydrothermal activation of belite cement (FABC-2-N) was clearly differentiated, mainly at early ages of hydration, for which the increase in the combined water was markedly higher than that of the belite cement that was hydrothermally activated in water. Important direct quantitative correlations were obtained among physicochemical parameters, such as the combined water, the BET surface area, the volume of nano-pores, and macro structural engineering properties such as the compressive mechanical strength.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.