Abstract
The current drive for sustainability demands recyclable matrices for composite materials. Vitrimers combine thermoset properties with reprocessability, but their mechanical performance in highly loaded applications, for instance, composites for aeronautics, is still to be demonstrated. This work presents the complete mechanical characterization of a new vitrimer reinforced with carbon fiber. This vitrimer formulation consists of functional epoxy groups and a new dynamic disulfide crosslinks-based hardener. The testing campaign for the vitrimer composites encompassed tension, compression, interlaminar shear strength (ILSS), in-plane shear (IPS), open-hole tension (OHT) and compression (OHC), filled-hole compression (FHC) and interlaminar fracture toughness tests under mode I and II. Test conditions included room temperature and high temperature of 70 °C and 120 °C, respectively, after moisture saturation. Tension and flexural tests also were applied on the neat vitrimer resin. The results compared well with those obtained for current aeronautic materials manufactured by Resin Transfer Molding (RTM). The lower values observed in compression and ILSS derived from the thermoplastic veils included as a toughening material. This work demonstrates that the vitrimer formulation presented meets the requirements of current matrices for aeronautic-grade carbon-reinforced composites.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.