Abstract
AbstractThe structural evolution of high density polyethylene (HDPE) during uniaxial tensile deformation, before and after irradiation by 1 MeV electrons, is in situ studied by synchrotron small angle X‐ray scattering (SAXS) and wide angle X‐ray diffraction (WAXD). Both the pristine and the irradiated HDPE exhibit three regions of deformation behavior. It is shown that the deformation in the first region is in accord with the change in long period of the lamellar structure. In the following two regions, both the strain‐induced melting and strain‐induced crystallization could occur. The tensile stress decreases with strain in the second region due to the dominant melting effect. In the third region, the synergistic effect of the melting and crystallization results in stress leveling off first, and then the tensile stress increases again because the crystallization effect becomes dominant at higher strains. For the irradiated HDPE, the irradiation‐induced crosslinking network slows down the deformation process. Compared to the pristine one, all the tensile stress is rather higher at a given strain for the irradiated HDPE. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014, 131, 40269.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.