Abstract
The TiN coating and Ti/TiN multilayer coatings were successfully fabricated on Ti6Al4V alloy by multi-arc ion plating. The Ti/TiN multilayer coatings with a total thickness of 4.6 μm and the TiN coating were prepared with a thickness of 5.6 μm. The XRD results indicate that the TiN phase of Ti/TiN multilayer coatings has a face-centered cubic crystal with the strong preferred orientation of (111) while the TiN coating has the face-centered cubic crystal structure with a preferred orientation of (200). For TiN coating, the hardness is (27.5 ± 1.9) GPa, the load-bearing capacity is (19.0 ± 3.6) N. For Ti/TiN multilayer coating, the hardness is (26.8 ± 1.7) GPa and the load-bearing capacity is (60.4 ± 4.0) N. The Ti/TiN multilayer coatings have excellent tribocorrosion resistance and lower coefficient of friction in simulated body fluid at 37 °C, compared with Ti6Al4V alloy and TiN coating, the tribocorrosion resistance of the multilayer coatings increased by approximately 58 and two times, respectively. The material loss which arises from tribocorrosion is not simply the summation of pure corrosion and pure wear loss, the synergism between corrosion and wear takes a large proportion of the total volume loss.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.