Abstract
Abstract Compounds with the general formula Mg1−x AlxB2 were obtained by two-step ceramic synthesis. All compounds were characterized by X-ray diffraction, NMR spectroscopy, and by four point probe resistivity measurements in various magnetic fields method. The diborides unit cell parameters were determined as a function of the Al mole fraction. With the vaues of x up to 0.40 (where x is the composition of the stock prepared for sintering), the unit cell parameters of Mg1−x AlxB2 are similar to those of pure MgB2 and the superconducting transition temperature was lowered. For stock compositions of 0:25 ≤ x ≤ 0:60, the products contain a superstructure, also superconducting phase, which becomes the only product at x = 0:50, and at x > 0:60 this phase is replaced by AlB2-based solid solutions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.