Abstract
Nanocrystalline Ga doped nickel ferrite [(NiFe2-xGaxO4 (x=0.0, 0.1, 0.3, 0.5 and 0.7)] powders have been synthesized by sol-gel auto-ignition method and the effect of non-magnetic gadillum content on the nanosize particles and magnetic properties has been studied. The X-ray diffraction (XRD) revealed that the powders obtained are single phase with spinel structure. The calculated grain size from XRD data have been verified using transmission electron microscopy (TEM). TEM photograph shows that the powders consist of nanometer sized grain. The size of nanoparticles decreases as the non magnetic Ga content increases. Magnetic hysteresis loops were measured at room temperature with maximum applied magnetic field of 20 KOe. As Ga content increases, the measured magnetic hysteresis curves became border and saturation magnetization (MS) increased up to x= 0.3 and further increase of x leads the magnetization to decrease. The results are explained according to the assumed cation distribution.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.