Abstract
Water-soluble cadmium telluride (CdTe) quantum dots (QDs) were synthesized using thioglycolic acid as capping agent; this reaction was carried out at pH = 10.2 and refluxed at 100°C for 18 h. The CdTe QDs prepared at various reflux times from 1 to 18 h were coated on the glass substrates to obtain thin films of the CdTe QDs with the same thickness. The CdTe thin films were characterized by X-ray diffraction, ultraviolet-vis spectroscopy, and photoluminescence spectroscopy. The absorption thresholds of the CdTe thin films are blueshifted by about 0.65 eV with respect to the bulk value (1.5 eV), due to the quantum size effect as expected from the nanocrystalline nature of the CdTe QDs. X-ray diffraction showed that the films consisted of small CdTe nanocrystallites, 2.91 to 3.57 nm in size, showing quantum size effects. The effects of temperature on the electrical properties of the films were studied in detail. Electrical resistivity measurements were carried out for different films in the temperature range from 343 to 463 K. It is shown that activation energy increases by increasing the reflux time.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.