Structural, magnetic and electrical transport properties for a series of La1−xSrxFe1−xMnxO3 (0.3≤x≤0.7) compounds

Abstract

Abstract The structural, electrical transport and magnetic properties have been studied for compounds: La 1− x Sr x Fe 1− x Mn x O 3 (0.3 ≤ x ≤ 0.7). The lattice parameter, a , first decreases with x , and followed by an increase when Sr 2+ and Mn 4+ was continuously doped. The cell parameters, b and c , slightly decrease with coupled substitution of Sr 2+ for La 3+ and Mn 4+ for Fe 3+ . In the paramagnetic temperature range, formation of magnetic clusters is suggested; the sizes of clusters decrease with x up to 0.5, following that they increase sharply with continuing doping. The electrical behaviors of all specimens demonstrate insulators and the electrical resistivity increases with content of Mn 4+ and Sr 2+ ions doped. A variable range hopping model is suitable to describe electrical transport process for the compounds at low temperature. At high temperature the electrical transport process can be described by bipolaron model for all compounds.