Abstract
Higher magnetic Mn doped Zn-Cr oxide nanoparticles with general compositional formula MxZn0.95-xCr0.05O have been synthesized by using sol-gel auto combustion technique. Room temperature X-ray diffraction (XRD) technique has been employed to study the structural and microstructural parameters of the as-prepared samples. XRD analysis confirms the phase purity and hexagonal wurtzite structure of all the samples. Replacement of Zn2+ ions by Mn2+ ions shifts peak positions slightly towards the lower angles which in turn expands the lattice lengths ‘a’ from 3.2487 to 3.2528 Å and ‘c’ from 5.2043 to 5.2118 Å. Crystallite size obtained from Scherrer equation was confirmed by Williamson – Hall (W-H) and size – strain plot methods (SSP). Both W-H and SSP methods reveals the tensile type strain for undoped sample and comprehensive type strain for Mn2+ doped samples. Magnetic properties were investigated by using vibrating sample magnetometer. Diluted ferromagnetic behaviour is observed for all the samples and saturation magnetization (MS) increases from 0.0514 to 0.1163 emu/gm. Two-probe technique was employed to understand the dielectric behaviour of the samples as a function of frequency. At lower frequency region, both dielectric constant () and dielectric loss tangent (tan ) shows higher values and decreases with the increasing applied frequency.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call