Abstract
A series of Sr2−xNdxNi2 Fe28−yCoyO46 (x=0.02, 0.04, 0.06, 0.08, 0.10 and y=0.1, 0.2, 0.3, 0.4, 0.5) X-type hexagonal ferrites has been prepared by sol–gel method at 1250°C for 6h. XRD analysis shows the single phase of the prepared ferrites material. The lattice constant values and c/a ratio shows that the present assembled material belongs to the family X-type hexagonal ferrites. The peaks in the FTIR spectra are the characteristics of the hexagonal ferrites. The crystallite size measured by Scherer formula is in good agreement with the crystallite size measured by TEM and HRTEM. The enhancement in the magnetic properties can easily be observed with the doping of rare earth element Nd3+ and divalent Co2+. Due to high saturation and low coercivity values the present material can be good microwave absorber. The temperature dependent saturation and remanance magnetization decreases monotonically with temperature. The minimum value of reflection loss enhances with the substituent and the attenuation constant results are in agreement with reflection loss results.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.